POLYPROPYLENE HOMOPOLYMER
EXTRUSION GRADE
HPP C30S
| PARAMETER | TEST METHOD | VALUE | UNIT |
| Melt flow rate (230 °C, 2.16 kg) | ISO 1133 | 6 | dg / min |
| Density | ISO 1183 | 0.9 | g/cm3 |
| Flexural modulus | ISO 178 | 1500 | N/mm2 |
| Tensile strength yield | ISO R 527 | 34 | N/mm2 |
| Elongation at yield | ISO R 527 | 13 | % |
| Izod Impact Strength (notched) at 23°C | ISO 180 | 4 | kJ/m2 |
| Hardness Shore D | ISO 868 | 71 | Points |
| Vicat softening point (9.8 N) | ISO 306/A | 155 | °C |
| H.D.T. (0.46 Mpa) | ISO 75/B | 112 | °C |
| Accelerated oven ageing in air
(forced circulation) at 150 °C |
ISO 4577 | 360 | hours |